Shaped, Flat, Square, Round, Fine Wire, Plated and Bare Wire AMS 5887, AMS 5888, AMS 5889, ASTM B166


Alloy 617 Description


Alloy 617 is a nickel-chromium-cobalt-molybdenum alloy.With an exceptional combination of metallurgical stability, strength, oxidation resistance at high temperatures and resistance to oxidation is enhanced by an aluminum addition, the alloy also resists a wide range of corrosive aqueous environments. Used in gas turbines for combustion cans, ducting, and transition liners; for petrochemical processing; for heat-treating equipment; and in nitric acid production. Standard product forms are round, forging stock, extruded section, plate, sheet, strip, pipe, tube, and wire.

Applications


Gas turbines for combustion components
Petrochemical processing
Heat-treating equipment
In nitric acid production

Chemistry Typical


Nickel: 44.5 min
Chromium: 20.0-24.0
Cobalt: 10.0-15.0
Molybdenum: 8.0-10.0
Aluminum: 0.8-1.5
Carbon: 0.05-0.15
Iron: 3.0 max.
Manganese: 1.0 max.
Silicon: 1.0 max.
Sulfur: 0.015 max.
Titanium: 0.6 max.
Copper: 0.5 max.
Boron: 0.006 max

Physical Properties


Density: 0.302 lb/in³, 8.36 g/cm³

Electrical Resistivity: ohm-cir-mil/ft (micro-ohm-m):
At 78°F (20°C): 736(1.222)
At 200°F (100°C): 448(1.245)
At 400°F (200°C): 757(1.258)
At 600°F (300°C): 764(1.268)
At 800°F (400°C): 770(1.278)
At 1000°F (500°C): 779(1.290)
At 1200°F (600°C): 793(1.308)
At 1400°F (700°C): 807(1.332)
At 1600°F (800°C): 803(1.342)
At 1800°F (900°C): 824(1.338)
At 2000°F (1000°C): —(1.378)

Specific Heat: BTU/lb-°F (J/Kg-°C):
At 78°F (20°C): 0.100(419)

Thermal Conductivity: BTU-in/hr-ft²-°F (W/m•°C):
At 78°F (20°C): 94(13.4)
At 200°F (100°C): 101(14.7)
At 400°F (200°C): 113(16.3)
At 600°F (300°C): 125(17.7)
At 800°F (400°C): 137(19.3)
At 1000°F (500°C): 149(20.9)
At 1200°F (600°C): 161(22.5)
At 1400°F (700°C): 173(23.9)
At 1600°F (800°C): 185(25.5)
At 1800°F (900°C): 197(27.1)
At 2000°F (1000°C): 209(28.7)

Mean Coefficient of Thermal Expansion: µin/in-°F(µm/m-°C):
78-200°F (20-100°C): 7.0 (11.6)
78-400°F (20-200°C): 7.2 (12.6)
78-600°F (20-300°C): 7.49 (13.1)
78-800°F (20-400°C): 7.6 (13.6)
78-1000°F (20-500°C: 7.7 (13.9)
78-1200°F (20-600°C): 8.0 (14.0)
78-1400°F (20-700°C): 8.4 (14.8)
78-1600°F (20-800°C): 8.7 (15.4)
78-1800°F (20-900°C): 9.0 (15.8)
78-2000°F (20-1000°C): 9.2 (16.3)

Modulus of Elasticity: KSI (MPa)
30.6 x 10³ (211 x 10³) in tension

Melting Range: 2430-2510°F (1332-1380°C):

Mechanical Properties at Room Temperature

Properties: Annealed Typical

Ultimate Tensile Strength: 95 KSI min (655MPa min)

Yield Strength: 35 KSI min (241 MPa min )

Elongation: 30% min

Properties:Tempered

Alloy 617 can be cold rolled to achieve the temper properties required by specific customers and/or manufacturing requirements. Contact Ulbrich Wire for details.

Additional Properties

Corrosion Resistance

Refer to NACE (National Association of Corrosion Engineers) for recommendations.

Standard Wire Finishes


Extra Clean: Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”

Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for decorative applications

Soap (round wire only): Soap is used as a lubricant in the drawing process and is not removed. It acts as a lubricant during customer part forming operation. 

A soap finish is available in tempered products.

Plated: Many plating options are available.
*Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.

Forms


Continuous Coils
Cut to lengths
Precision cutting

Heat Treatment


Alloy 617 is non hardenable by heat treatment.

Welding


For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”.
* Inconel® 617 is a registered trademark of the Special Metals Corp.

Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.

Contact Us

Full Name
Title
Company
City, State, Country
Email
Phone (Optional)
Message (Optional)