(Commercially Pure Titanium: Grade 1) Strip, Coil, Foil, Wire, ASTM B265 GR1, ASTM F67

Applications

Titanium: Grade 1 Description

Commercially Pure Titanium Grade 1 is one of the softest and most ductile grades exhibiting the greatest formability. It has excellent corrosion resistance property, excellent weldability and is used in a wide variety of applications. This grade material is mainly used in marine and chemical industries where the parts are subjected to very harsh environments. This material is also used for fabricating anodes for cathodic protection applications.

Chemistry Typical

Titanium: Balance
Iron: 0.20 max
Oxygen: 0.18 max
Carbon: 0.08 max
Nitrogen: 0.03 max
Hydrogen: 0.015 max
Residuals each 0.10 max, total 0.40 max

Physical Properties of Titanium: Grade 1

Density: 0.163 lbs/in3 , 4.51 g/cm3

Mean Coefficient of Thermal Expansion, in/in/° F (mm/m/° C):
70 - 212 ° F (20 - 100 ° C): 4.78 x 10-5 (8.6)

Thermal Conductivity: BTU-in/h-ft-° F (W/m-° K):
At 70 ° F (21 °C): 111 (16)

Modulus of Elasticity, ksi (MPa): 15.2 x 103 (105 x 103) in tension

Melting Point: 3040 ° F (1670 ° C)

Forms

Coil - Strip, Foil, Ribbon
Wire - Profile, Round, Flat, Square

Mechanical Properties at Room Temperature

Properties Annealed:

Ultimate Tensile Strength: 35 KSI min (240 MPa min )
Yield Strength (0.2% offset): 25 - 45 KSI (170 - 310 MPa )
Elongation: 24%

Properties: Tempered

Titanium Grade 1 can be cold rolled to various tempers. Contact Ulbrich Technical Service for additional information.

Additional Properties

Corrosion Resistance

Refer to NACE (National Associate of Corrosion Engineers) for recommendations.

Finishes

#1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
#2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process.
#2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA - Bright annealed cold rolled and bright annealed
#CBA - Course bright annealed cold rolled matte finish and bright anneal
#2 - Cold Rolled
#2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part.
Polished - Various grit finish for specific polish finished requirements.

* Not all finishes are available for all alloys- Contact Ulbrich Sales for more information.

Wire Finishes

XC - Extra clean. Bright annealed or bright annealed and cold rolled Grease - Ultra bright finish for decorative applications
Soap - Soap is not removed from tempered wire to act as a lubricant. * Contact Ulbrich Wire for custom finishes.

Heat Treatment

Titanium Grade 1 can only be hardened by cold work.

Welding Titanium: Grade 1

For best results refer to: SSINA's "Welding of Stainless Steels and Other Joining Methods".


Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels & Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the 'applications' noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.


Contact Us

Full Name
Title
Company
City, State, Country
Email
Phone (Optional)
Message (Optional)