(Nickel Alloy HC22) Strip, Foil, Wire, ASTM B575


Bellows, flue gas scrubber components, nuclear fuel reprocessing and sour gas production 


Hastelloy® C-22 is a most versatile nickel-chromium-molybdenum-tungsten alloy with improved resistance to both uniform and localized corrosion as well to a wide variety of mixed industrial chemicals. HC-22 has corrosion resistance superior to other Ni-Cr-Mo alloys including C-276, C-4 and 625. The C-22 alloy exhibits superior weldability. 

Chemistry Typical 

Nickel: Balance 
Chromium: 20.00 - 22.50 
Molybdenum: 12.50 - 14.50 
Iron: 2.00 - 6.00 
Tungsten: 2.50 - 3.00 
Cobalt: 2.50 max 
Carbon: 0.10 max 
Silicon: 0.08 max 
Manganese: 0.50 max 
Phosphorus: 0.02 max 
Vanadium: 0.35 max 

Physical Properties 

Density: 0.314 lbs/in3, 8.69 g/cm3

Mean Coefficient of Thermal Expansion: in/in/° F (mm/m/°C): 
70 - 212 °F (20 - 100 °C): 6.9 x 10-5 (12.4) 

Thermal Conductivity: BTU- in/h-ft- (W/m- °K):
70 °F (21 °C): 70 (10.1) 

Modulus of Elasticity: ksi (MPa) 
29.9 x 103 (206 x 103) in tension 

Melting Point: 2550 °F (1400 °C) 


Coil - Strip, Foil, Ribbon  Wire - Profile, Round, Flat, Square 

Mechanical Properties at Room Temperature 

Annealed Typical 

Ultimate Tensile Strength: 100 KSI min (690 MPa min) 
Yield Strength: (0.2% offset) 45 KSI min (310 MPa min) 
Elongation: 45% min 
Hardness: Rb 100 max (aim) 


Hastelloy® C-22 can be cold rolled to various tempers. Contact Ulbrich Technical Service for additional information. 

Additional Properties 

Corrosion Resistance

Refer to NACE (National Associate of Corrosion Engineers) for recommendations. 


#1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required. 
#2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process.  #2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D. 
#BA- Bright annealed cold rolled and bright annealed 
#CBA- Course bright annealed cold rolled matte finish and bright anneal 
#2 - Cold Rolled  #2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part.  Polished - Various grit finish for specific polish finished requirements. 
* Not all finishes are available in all alloys - Contact Ulbrich Sales for more information.

Wire Finishes

XC - Extra Clean Bright Annealed or Bright Annealed and Cold Rolled Grease - Ultra bright finish (for decorative applications)  Soap - Soap coating on tempered wire to act as lubricant.  * Contact Ulbrich Wire for custom wire finishes

Heat Treatment

Hastelloy® C-22 cannot be hardened heat treating. 


For best results refer to: SSINA's "Welding of Stainless Steels and Other Joining Methods". 

Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels & Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the 'applications' noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.

Contact Us

Full Name
City, State, Country
Phone (Optional)
Message (Optional)