Strip, Coil, Foil Wire, AMS 5503, ASTM A240
Architectural, automotive parts, cooking utensils, fasteners, food processing, oil burners parts, television cones, tobacco machinery parts
Type 430Li is a chromium ferritic stainless steel similar to 430, with moderate corrosion and heat resistance. It is non-hardenable by heat treatment, magnetic and can be readily formed into most desired shapes. Type 430Li has low interstitials providing better ductility over regular 430.
Carbon: 0.022 max
Manganese: 1.00 max
Silicon: 1.00 max
Chromium: 16.00 - 18.00
Nickel: 0.50 max
Molybdenum: 0.50 max
Phosphorus: 0.040 max
Sulfur: 0.030 max
Copper: 0.50 max
Density: 0.28 lbs/in3 7.74 g/cm3
Electrical Resistivity: microhm-in (microhm-cm):
68 ° F (20 ° C): 23.68 (60)
Specific Heat: BTU/lbl° F (kJ/kg•K):
32 - 212 ° F (0 - 100 °C): 0.11 (0.46)
Thermal Conductivity: BTU/hr/ft2/ft/° F (W/m•K)
At 212 °F (100 °C): 15.1 (26.1)
At 932 °F (500 °C): 15.2 (26.3)
Mean Coefficient of Thermal Expansion: in/inl° F (µm/m•K):
32 -212 ° F (0 - 100 °C): 5.8 x 10-5 (10.4)
32-1000 ° F (0- 538 °C): 6.3 x 10-5 (11.4)
Modulus of Elasticity: ksi (MPa)
29 x 103 (200 x 103) in tension
Magnetic Permeability: Magnetic
Melting Range: 2600 - 2750 ° F (1427 - 1510 °C)
Coil -Strip, Foil, Ribbon Wire -Profile, Round, Flat, Square
Mechanical Properties at Room Temperature
Ultimate Tensile Strength: 65 KSI min (450 MPa min)
Yield Strength (0.2% offset): 30 KSI min (205 MPa min)
Elongation: 22% min
Hardness: Rb 89 max
Type 430Li can be rolled to various tempers. Contact Ulbrich Technical Services if tempered properties are required.
Refer to NACE (National Association of Corrosion Engineers) for recommendations.
# 1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
# 2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. # 2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA- Bright annealed cold rolled and bright annealed
#CBA- Course bright annealed cold rolled matte finish and bright anneal
#2 - Cold Rolled
# 2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished - Various grit finish for specific polish finished requirements.
* Not all finishes are available for all alloys - Contact Ulbrich Sales for more information.
XC - Extra clean bright annealed or bright annealed and cold rolled Grease - Ultra-bright finish (for decorative applications) Soap - Soap is not removed from tempered wire to act as a lubricant. * Contact Ulbrich Wire for custom wire finishes.
Type 430Li is readily drawn and formed. Its drawing characteristics are similar to those of low carbon steel, although it is stronger in the annealed condition and will require stronger tooling and increased power. It is also adaptable to most hot-forming operations. Better ductility than straight 430.
It is non-hardenable by heat treatment.
For best results refer to: SSINA's "Welding of Stainless Steels and Other Joining Methods".
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels & Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the 'applications' noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.