Hastelloy® G-30 UNS N06030
Hastelloy® G-30 is an improved version of nickel-chromium-iron-molybdenum-copper alloy G-3.
(Nickel Alloy G-30) Strip, Coil, Foil, Wire, ASTM B582
Gas scrubbers, acid production and pickling
Hastelloy® G-30 is an improved version of nickel-chromium-iron-molybdenum-copper alloy G-3. With higher chromium, added cobalt and tungsten, the G-30 shows superior corrosion resistance over most other nickel and iron based alloys in commercial phosphoric acids as well as complex environments containing highly oxidizing acids. The resistance of the alloy to the formation of grain boundary precipitates in the heat-affected zone makes it suitable for use in most chemical process applications in the as-welded condition.
Chromium: 28.00 - 31.50
Iron: 13.00- 17.00
Molybdenum: 4.00 - 6.00
Copper: 1.00 - 2.40
Cobalt: 5.00 max
Manganese: 1.50 max
Columbium + Tantalum: 0.30-1.50
Carbon: 0.03 max
Phosphorus: 0.04 max
Silicon: 0.80 max
Sulfur: 0.02 max
Density: 0.297 lbs/in3 , 8.22 g/cm3
Mean Coefficient of Thermal Expansion: in/in/ °F (mm/m/ °C):
70-212 °F (20- 100 °C): 7.1 x 10-6 (12.8)
Thermal Conductivity: BTU-in/h-ft-°F (W/m-°K): 70 °F (21 °C): 71 (10.2)
Modulus of Elasticity: ksi (MPa) 29.3 x 103 (202 x 103) in tension
Melting Point (approximate): 2550 °F (1399 °C)
Coil - Strip, Foil, Ribbon Wire - Profile, Round, Flat, Square
Mechanical Properties at Room Temperature
Ultimate Tensile Strength: 85 KSI min (586 MPa min)
Yield Strength: (0.2% offset) 35 KSI min (241 MPa min)
Elongation: 30% min
Contact Ulbrich Technical Service for additional information.
Hastelloy® G-30 shows superior corrosion resistance in commercial phosphoric acids as well as complex environments containing highly oxidizing acids such as nitric/hydrochloric, nitric/ hydrofluoric and sulfuric acids. Refer to NACE (National Associate of Corrosion Engineers) for recommendations.
#1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
#2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. #2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA- Bright annealed cold rolled and bright annealed
#CBA- Course bright annealed cold rolled matte finish and bright anneal
#2 - Cold Rolled #2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the form part. Polished -Various grit finish for specific polish finished requirements.
* Not all finishes are available for all alloys - Contact Ulbrich Sales for more information.
XC - Extra Clean Bright Annealed or Bright Annealed and Cold Rolled Grease - Ultra bright finish (for decorative applications) Soap - Soap coating on tempered wire to act as lubricant. * Contact Ulbrich Wire for custom wire finishes.
Hastelloy® G-30 has good ductility and may be formed by conventional methods.
Hastelloy® G-30 can be hardened by cold working.
For best results refer to: SSINA's "Welding of Stainless Steels and Other Joining Methods".
Hastelloy® G-30 is a grade of Hastelloy® which is a nickel-molybdenum alloy. There are many different grades of Hastelloy®, which includes G-30. Grades of Hastelloy® have each been optimized for a specific purpose. Molybdenum makes Hastelloy® harder and stronger at high temperatures. This alloying element and the characteristics it imbues into the material also makes it great for welding applications. These nickel alloys are easily fabricated and formed. They also exhibit good ductility and are able to be cold worked.
All grades of Hastelloy® are considered to be a corrosion resistant alloy because each grade exhibits superior resistance to various corrosive environments. Hastelloy® has outstanding resistance to highly oxidizing corrosives such as oxidizing salts and reducing agents, making it a great alloy to specify for applications used in moderate to severe corrosive environments.
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels & Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the 'applications' noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.