Alloy 230 Description


Alloy 230 is a nickel-chromium-tungsten-molybdenum alloy which combines excellent high temperature strength, oxidation resistance (up to 2100°F), nitriding resistance and long term stability. It is particularly effective for very long-term applications at temperatures of 1200°F (649°C) or more and is capable of outlasting stainless steels and nickel alloys by as much as 100 to 1 depending upon the temperature.Alloy 230 is a solid-solution-strengthened material which combines excellent high-temperature strength with good fabricability at room temperature.

Applications


Resistance heater components
Heat treating baskets and trays
Wire annealing fixtures
Chemical process components

Chemistry Typical


Nickel: 47.00-65.00
Iron: 3.00 max
Chromium: 20.00 – 24.00
Cobalt: 5.00 max
Molybdenum: 1.00 – 3.00
Tungsten: 13.00 – 15.00
Carbon: 0.05-0.15
Manganese: 0.30-1.00
Silicon: 0.25-0.75
Aluminum: 0.20-0.50
Lanthanum: 0.005-0.05
Phosphorus: 0.03 max
Sulfur: 0.015 max
Boron: 0.015 max
Titanium: 0.10 max
Copper: 0.50 max

Physical Properties


Density: 0.327 lbs/in³, 9.05 g/cm³

Specific Heat: BTU/lb/°F (J/kg•K):
At 70°F (21°C): .0095 (397)

Mean Coefficient of Thermal Expansion: in/in/°F (mm/m/°C):
70- 212°F (20- 100°C): 7.0 x 10 (12.7)

Thermal Conductivity: BTU-in/h-ft-°F (W/m-°K):
70°F (21°C): 62 (8.9)

Modulus of Elasticity: KSI (MPa)
30.6 x 10³ (210 x 10³) in tension

Melting Range: 2375-2500F (1300-1374°C)

Mechanical Properties at Room Temperature

Properties: Annealed


Ultimate Tensile Strength: 110 KSI min (760 MPa min)
Yield Strength (0.2% offset): 45 KSI min (310 MPa min)
Elongation: 40% min


Properties Tempered

Alloy 230 can be cold rolled to achieve the temper properties required by specific customers and/or manufacturing requirements. Contact Ulbrich Wire for details.

Additional Properties


Corrosion Resistance


Refer to NACE (National Association of Corrosion Engineers) for recommendations.

Standard Wire Finishes


Extra Clean: Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”

Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for decorative applications

Soap (round wire only): Soap is used as a lubricant in the drawing process and is not removed. It acts as a lubricant during customer part forming operation. 

A soap finish is available in tempered products.
Plated: Many plating options are available.

*Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.

Forms


Continuous Coils
Cut to lengths
Precision cutting
Heat Treatment
Alloy 230 cannot be hardened heat treating

Welding


For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”

Haynes® 230 is a registered trademark of Haynes Alloys.

Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.

Contact Us

Full Name
Title
Company
City, State, Country
Email
Phone (Optional)
Message (Optional)