Strip, Coil, Foil, Wire, QQN286 

Applications 

Pump components, doctor blades and scrapers, oil well drill collars and cable wrap, marine instruments, electronic components, springs, valve tray, and submarine parts 

Description 

Monel® K500 (Alloy K500) is a Nickel Copper alloy which combines the excellent corrosion resistance of Alloy 400 with the added advantages of greater strength and hardness. The increase in strength and hardness is a result of the precipitation hardening capability gained by the additions of titanium and aluminum. 

Chemistry Typical 

Nickel: 63.0 min 
Copper: 27.0-33.0 
Aluminum: 2.30-3.15 
Titanium: 0.35-0.85 
Iron: 2.00 MAX 
Phosphorus 0.020 max 
Sulfur: 0.010 max 
Silicon: 0.050 max 
Manganese: 1.50 max 
Carbon: 0.25 max 

Physical Properties 

Density: 0.305 lbs/in3, 8.44 g/cm3

Mean Coefficient of Thermal Expansion: in/in/° F (mm/m/° C):
70 - 212 °F (20 - 100 ° C): 7.6 x 10-5 (13.7)

Modulus of Elasticity: KSI (MPa)
26 x 10 3 (179 x 10 3) in Tension 

Magnetic Permeability, H = 200: Annealed <1.002 

Melting Point: 2460 °F (1350 °C) approx. 


Forms 


Coil - Strip, Foil, Ribbon 
Wire - Profile, Round, Flat, Square 


Mechanical Properties at Room Temperature 


Properties: Annealed 

Ultimate Tensile Strength: 90 KSI min (620 MPa min)
Yield Strength: 40 KSI min (275 MPa min)
Elongation: 30% min 
Hardness: 
HV 170 max: gauges s 0.010 inches
Rb 85 max: gauges> 0.010 inches 

Properties: Tempered

Monel® K500 (Alloy K500) can be supplied in half hard a full hard temper. Contact Ulbrich Technical Service for additional information. 

Heat Treat Capabilities

Ultimate Tensile Strength: 130 KSI min (895 MPa min)
Yield Strength (0.2% offset): 90 KSI min (620 MPa min)
Elongation: 15% min 
Hardness: Re 24 min 

Half Hard & Aged

Ultimate Tensile Strength: 145 KSI min (1000 MPa min)
Yield Strength (0.2% offset): 110 KSI min (760 MPa min)
Elongation: 8% min 
Hardness: Re 30 min 

Full Hard & Aged

Ultimate Tensile Strength: 170 KSI min (1170 MPa min)
Yield Strength (0.2% offset): 140 KSI min 
Elongation: 5% min 
Hardness: Re 34 min 

Additional Properties

Corrosion Resistance

Refer to NACE (National Associate of Corrosion Engineers) for recommendations. 

Finishes

#1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required. 
#2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. 
#2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D. 
#BA- Bright annealed cold rolled and bright annealed 
#CBA- Course bright annealed cold rolled matte finish and bright anneal 
#2 - Cold Rolled 
#2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. 
Polished - Various grit finish for specific polish finished requirements. 
* Not all finishes are available for all alloys - Contact Ulbrich Sales for more information.

Wire Finishes

XC - Extra Clean Bright Annealed or Bright Annealed and Cold Rolled Grease - Ultra bright finish (for decorative applications) 
Soap - Soap coating on tempered wire to act as lubricant 
* Contact Ulbrich Wire for custom finishes.

Heat Treatment

Monel® KSOO (Alloy KSOO) can be hardened by cold working and by heat treating. 

Welding

For best results refer to: SSINA's "Welding of Stainless Steels and Other Joining Methods". 


Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels & Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the 'applications' noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.


Contact Us

Full Name
Title
Company
City, State, Country
Email
Phone (Optional)
Message (Optional)