(Nickel B-3) Strip, Foil, Wire, ASTM B333

Applications 

Aircraft, furnace and chemical process components, honeycombs and gas turbine combustion section components 

Description 

Hastelloy® B-3 is a nickel- molybdenum alloy with excellent resistance to pitting, corrosion and stress-corrosion cracking, plus thermal stability superior to that of alloy B-2. This alloy has also  great resistance to knife-line and heat-affected zone attack. The improved thermal stability of B-3 alloy minimizes the problems associated with fabrication of B-2 alloy components. This is due to the reduced tendency to precipitate deleterious inter-metallic phases in B-3 alloy, thereby, affording it greater ductility than B-2 alloy during and following various thermal cycling conditions. 

Chemistry Typical 

Nickel: 65.0 min 
Chromium: 1.00-3.00 
Molybdenum: 27 .00-32.00 
Iron: 1.0-3.0 
Cobalt: 3.0 max 
Tungsten: 3.0 max 
Manganese: 3.0 max 
Aluminum: 0.50 max 
Titanium: 0.20 max 
Silicon: 0.10 max 
Carbon: 0.01 max 
Copper: 0.20 max 

Physical Properties 

Density: 0.333 lbs/in3, 9.22 g/cm3

Electrical Resistivity: microhm-in, (microhm-cm): 
70 ° F (21 °C)- 53.8 (137)

Specific Heat: BTU/lbl° F (J/kg•K):
32 - 212 ° F (0 - 100 °C}: 0.089 (373)

Mean Coefficient of Thermal Expansion: in/inl° F (mm/ml°C):
70 - 212 °F (20 - 100 °C): 5.7 x 10·6 (10.6)

Thermal Conductivity: BTU-in/h-ft-° F (W/m-° K):
70 ° F (21 °C): 78 (11.2)

Modulus of Elasticity: ksi (MPa) 
31.4 x 103 (216 x 103) in tension 

Melting Point: 2500 - 2585 °F (1370 - 1418 °C)

Forms 

Coil - Strip, Foil, Ribbon  Wire - Profile, Round, Flat, Square 

Mechanical Properties at Room Temperature 

Annealed: Typical 

Ultimate Tensile Strength: 125 KSI (860 MPa) 
Yield Strength: (0.2% offset) 60 KSI (420 MPa) 
Elongation: 50% 

Tempered

Hastelloy® B-3 can be cold rolled to various tempers. Contact Ulbrich Technical Service for additional information. 

Additional Properties

Corrosion Resistance 

Refer to NACE (National Associate of Corrosion Engineers) for recommendations. 

Finishes

#1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required. 
#2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process.  #2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA- Bright annealed cold rolled and bright annealed 
#CBA- Course bright annealed cold rolled matte finish and bright anneal 
#2 - Cold Rolled  #2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part.  Polished - Various grit finish for specific polish finished requirements. 

* Not all finishes are available in all alloys - Contact Ulbrich Sales for more information.

Wire Finishes

XC - Extra Clean Bright Annealed or Bright Annealed and Cold Rolled Grease - Ultra bright finish (for decorative applications)  Soap - Soap coating on tempered wire to act as lubricant. 

* Contact Ulbrich Wire for custom wire finishes.

Heat Treatment

Hastelloy® B-3 cannot be hardened heat treating. 

Welding

For best results refer to: SSINA's "Welding of Stainless Steels and Other Joining Methods". 




Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels & Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the 'applications' noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.

 

Contact Us

Full Name
Title
Company
City, State, Country
Email
Phone (Optional)
Message (Optional)