201 |
Chromium nickel manganese steel was developed as a satisfactory (more...) |
0.15
|
3.5 - 5.5
|
16.0 - 18.0
|
|
|
A 240, A 666
|
0.28 |
|
301 |
Chromium nickel steel capable of attaining high tensile strength (more...) |
0.15
|
6.0 - 8.0
|
16.0 - 18.0
|
|
5517, 5519, 5518
|
A 240, A 666
|
0.29 |
|
302 |
General purpose chromium nickel stainless steel. Its corrosion (more...) |
0.15
|
8.0 - 10.0
|
17.0 - 19.0
|
|
5516
|
A 240, A 666
|
0.29 |
|
304 |
Low carbon chromium nickel stainless and heat resisting steel (more...) |
0.08
|
8.0 - 10.5
|
18.0 - 20.0
|
|
5513
|
A 240, A 666
|
0.29 |
|
304L |
Very low carbon chromium nickel steel with general corrosion (more...) |
0.03
|
8.0 - 12.0
|
18.0 - 20.0
|
|
5511
|
A 240, A 666
|
0.29 |
|
305 |
A high corrosion-resistant alloy with low rate of work hardening, (more...) |
0.12
|
10.0 - 13.0
|
17.0 - 19.0
|
|
5514
|
A 240
|
0.29 |
|
309 |
High corrosion-resistant, chromium nickel grade with carbon limited (more...) |
0.08
|
12.0 - 15.0
|
22.0 - 24.0
|
|
5523
|
A 240, A 166
|
0.29 |
|
310 |
Similar to 309 with higher resistance to corrosion and oxidation (more...) |
0.25
|
19.0 - 22.0
|
24.0 - 26.0
|
|
5521
|
A 240, A 167
|
0.29 |
|
316 |
Chromium nickel stainless and heat resisting steel with superior (more...) |
0.08
|
10.0 - 14.0
|
16.0 - 18.0
|
2.0 - 3.0
|
5524
|
A 240, A 666
|
0.29 |
|
316L |
Low carbon chromium nickel stainless steel with general corrosion (more...) |
0.03
|
10.0 - 14.0
|
16.0 - 18.0
|
2.0 - 3.0
|
5507
|
A 240, A 666
|
0.29 |
|
316TI |
Ti stabalized version of 316 with resistance to sensitization. (more...) |
0.08
|
10.0 - 14.0
|
16.0 - 18.0
|
2.0 - 3.0
|
|
A 240
|
0.29 |
|
317L |
Similar to 316L but with additional molybdenum to improve corrosion (more...) |
0.03
|
11.0 - 15.0
|
18.0 - 20.0
|
3.0 - 4.0
|
|
A 240
|
0.29 |
|
321 |
Chromium nickel steel containing titanium.Recommended for parts (more...) |
0.08
|
9.0 - 12.0
|
17.0 - 19.0
|
|
5510
|
A 240
|
0.29 |
|
347 |
Chromium nickel steel containing columbium and tantalum which (more...) |
0.08
|
9.0 - 13.0
|
17.0 - 19.0
|
|
5512
|
A 240
|
0.29 |
|
CARPENTER® 20 CB3, 10 |
A highly corrosion-resistant alloy used in the chemical industry (more...) |
0.06
|
32.5 - 35.0
|
19.0 - 21.0
|
2.0 - 3.0
|
|
B 463
|
0.289 |
|
2304 |
A lean austenitic-ferritic duplex stainless steel with general (more...) |
0.03
|
3.0 - 5.5
|
21.5 - 24.5
|
|
|
A 240
|
0.28 |
|
2205 |
A nitrogen, molybdenum enhanced austenitic-ferritic duplex stainless (more...) |
0.03
|
4.5 - 6.5
|
22.0 - 23.0
|
3.0 - 3.5
|
|
A 240
|
0.28 |
|
2507 |
A super austenitic-ferritic duplex stainless steel with exceptional (more...) |
0.03
|
6.0 - 8.0
|
24.0 - 26.0
|
3.0 - 5.0
|
|
A 240
|
0.28 |
|
430 |
General purpose grade, corrosion-resistant, straight chromium (more...) |
0.12
|
|
16.0 - 18.0
|
|
5503
|
A 240
|
0.28 |
|
430LI |
Similar to straight 430 in corrosion and mechanical properties. (more...) |
0.022
|
|
16.0 - 18.0
|
|
|
|
0.28 |
|
434 |
Modification of Grade 430 designed for automotive trim and resistance (more...) |
0.12
|
|
16.0 - 18.0
|
0.75 - 1.25
|
|
A 240
|
0.28 |
|
444 |
A low carbon, low nitrogen, ferritic that provides pitting and (more...) |
0.025
|
1.0 max.
|
17.5 - 19.5
|
1.75 - 2.50
|
|
A 240
|
0.28 |
|
Grade 9 Ti 3-2.5 |
Alpha-Beta alloy-considered very weldable. Superior to high strength (more...) |
0.05
|
|
|
|
|
B 265
|
0.163 |
|
Ti 15-3-3-3 |
A cold formable metastable beta alloy available in foil and strip (more...) |
0.05
|
|
|
|
|
B 265
|
0.172 |
|
Grade 21 Ti Beta 21 S |
A cold formable metastable beta alloy available in foil and strip (more...) |
0.05
|
|
|
|
|
B 265
|
0.178 |
|
Grade 5, Ti 6-4 |
Grade 5 is the work horse of all titanium grades. It is also (more...) |
|
|
|
|
|
B265
|
0.16 |
|
Ti 6-2-4-2 |
Ti 6Al-2Sn-4Zr-2Mo has good tensile creep and fatigue properties (more...) |
|
|
|
2.2 max
|
|
|
0.164 |
|
410 |
General purpose corrosion and heat resisting chromium steel. (more...) |
0.15
|
|
11.5 - 13.5
|
|
5504
|
A 240
|
0.28 |
|
420 |
Chromium steel capable of hardening to a maximum of approximately (more...) |
.15 min.
|
|
12.0 - 14.0
|
|
5506
|
A-176
|
0.28 |
|
440A |
High carbon grade, high chromium, capable of being heat treated (more...) |
.60 - .75
|
|
16.0 - 18.0
|
|
|
|
0.28 |
|
17-7PH®4 |
A chromium nickel stainless steel with characteristics of good (more...) |
0.09
|
6.5 - 7.75
|
16-18.0
|
|
5528
|
A-693
|
0.282 |
|
17-4PH®4 |
Precipitation hardening stainless steel with high strength and (more...) |
0.07
|
3.0 - 5.0
|
15.0 - 17.5
|
|
5604
|
A-693 (Type 630)
|
0.28 |
|
PH15-7Mo®4 |
Similar to 17-7PH. alloy, but with molybdenum added for higher (more...) |
0.09
|
6.50 - 7.7
|
14.0 - 16.0
|
2.0 - 3.0
|
5520
|
A-693
|
0.282 |
|
A2864 |
An iron, nickel chromium alloy designed for service up to 1300°F (more...) |
0.08
|
24.0 - 27.0
|
13.5 - 16.0
|
1.0 1.75
|
5525
|
|
0.286 |
|
AM 3508 |
Similar to 17-7PH. alloy and PH15-7Mo. alloy, but with slightly (more...) |
.07 - .11
|
4.0 - 5.0
|
16.0 - 17.0
|
2.5 - 3.2
|
5548
|
A-693
|
0.286 |
|
NIOBIUM TYPE 1 |
Pure niobium, reactor grade, high melting point, corrosion resistant (more...) |
|
|
|
|
|
B 393
|
0.31 |
|
NITINOL |
NITINOL (an acronnym for Nickel Titanium Naval Ordinance Laboratory) (more...) |
|
|
|
|
|
|
0.235 |
|
NIOBIUM TYPE 2 |
a commercial grade alloy with an extremely high melting point (more...) |
|
|
|
|
|
B 393
|
0.31 |
|
ZIRCONIUM 702 |
a refractory metal with excellent corrosion resistance. Zirconium (more...) |
|
|
|
|
|
B551 |
|
|
NICKEL 200 |
Commercially pure nickel. High corrosion resistance. Used in (more...) |
0.15
|
99.0 min.
|
|
|
|
B 162
|
0.322 |
|
NICKEL 201 |
Similar to Nickel 200 except with a lower carbon content for (more...) |
0.02
|
99.0 min.
|
|
|
5553
|
B 162
|
0.322 |
|
PERMANICKEL 300 |
Age - hardenable, high nickel alloy, with very good thermal electrical (more...) |
0.4
|
Bal
|
|
|
|
|
0.316 |
|
MONEL® 4001 |
A solid solution alloy with high strength and toughness over (more...) |
0.3
|
63.0 min.
|
|
|
|
B 127
|
0.318 |
|
MONEL® K-5001 |
Similar to Monel. 400™ but with higher tensile strength; (more...) |
0.25
|
63.0 min.
|
|
|
|
|
0.305 |
|
INCONEL® 6001 |
Has high corrosion and heat resistance combined with excellent (more...) |
0.15
|
72.0 min.
|
14.0 - 17.0
|
|
5540
|
B 168
|
0.304 |
|
INCONEL® 6251 |
Outstanding corrosion resistance with excellent fabricability. (more...) |
0.1
|
58.0 min.
|
20.0 - 23.0
|
8.0 - 10.0
|
5599, 5869, 5879
|
B 443
|
0.305 |
|
INCONEL® 7181 |
High strength and corrosion resistance for use in temp. ranges (more...) |
0.08
|
50.0 - 55.0
|
17.0 - 21.0
|
2.80 - 3.30
|
5596, 5597
|
B670
|
0.296 |
|
INCONEL® X-7501 |
A precipitation hardening nickel-chromium alloy with useful strength (more...) |
0.08
|
70.0 min.
|
14.0 - 17.0
|
|
5542, 5598
|
|
0.3 |
|
INCOLOY® 8001 |
Nickel-iron-chromium alloy that is carburization resistant at (more...) |
0.1
|
30.0 - 35.0
|
19.0 - 23.0
|
|
5871
|
B 409
|
0.29 |
|
INCOLOY® 8251 |
An alloy that is highly resistant to ggressively corrosive environments (more...) |
0.05
|
38.0 - 46.0
|
19.5 - 23.5
|
2.5 - 3.5
|
|
B 424
|
0.293 |
|
Ni-SpanC® 9021 |
A nickel-iron-chromium alloy used in precision spring applications (more...) |
0.06
|
41.0 - 43.5
|
4.9 - 5.75
|
|
|
|
0.293 |
|
HASTELLOY® C-2762 |
Used in chemical industry for resistance to oxidizing agents. (more...) |
0.01
|
Bal
|
14.5 - 16.5
|
15.0 - 17.0
|
|
B 575
|
0.321 |
|
HASTELLOY C-22 |
A versatile nickel chromium molybdenum tungsten alloy with resistance (more...) |
0.015
|
Bal
|
20.0 - 22.5
|
12.5 - 14.5
|
|
B 575
|
0.314 |
|
HASTELLOY G-30 |
High chromium nickel base alloy with superior corrosion resistance (more...) |
0.03
|
Bal
|
28.0 - 31.5
|
4.0 - 6.0
|
|
B 582
|
0.297 |
|
HASTELLOY® B-3 |
Used in chemical industry for resistance to hydrochloric acid, (more...) |
0.01
|
65.0 min.
|
1.0 - 3.0
|
27.0 - 32.0
|
|
|
0.333 |
|
HASTELLOY® X2 |
Jet engine components for afterburner sections, blades, tailpipes, (more...) |
0.05 - 0.15
|
Bal
|
20.5 - 23.0
|
8.0 - 10.0
|
|
|
0.297 |
|
HAYNES® 2142 |
Nickel based precipitation strengthened alloy with oxidation (more...) |
0.05
|
Bal
|
15.0 - 17.0
|
0.5 max
|
|
|
0.29 |
|
HAYNES® 2302 |
Nickel-chromium-tungsten-molybdenum alloy with outstanding resistance (more...) |
0.05 - 0.15
|
Bal
|
20.0 - 24.0
|
1.0 - 3.0
|
|
|
0.319 |
|
HAYNES® 2422 |
Age hardenable, nickel alloy for use up to 1300°F. Low thermal (more...) |
0.03
|
Bal
|
7.0 - 9.0
|
24.0 - 26.0
|
|
|
0.327 |
|
MONEL® 4011 |
An alloy mainly used for thermal and electronic applications. (more...) |
0.5
|
44.0 min.
|
|
|
|
B267
|
0.321 |
|
HAYNES® 1882 |
A cobalt-based alloy with excellent high temperature strength (more...) |
0.05-0.15
|
20.0 - 24.0
|
21.0 - 23.0
|
|
|
|
0.324 |
|
HAYNES® 25 L-6052 |
Jet engine components, combustion chambers, afterburner parts. (more...) |
0.05 - 0.15
|
9.0 - 11.0
|
19.0 - 21.0
|
|
|
|
0.33 |
|
WASPALOY6 |
Jet engine turbine wheels, buckets, spacers, shafts. Good for (more...) |
0.03 - 0.10
|
Bal
|
18.0 - 21.0
|
3.5 - 5.0
|
5544
|
|
0.294 |
|
HAYNES® 263 |
nickel base gamma prime strengthened alloy with 19% to 21% cobalt (more...) |
|
|
|
|
|
5872
|
|
|
Grade 1 |
Low residual grade of commercially pure titanium available in (more...) |
0.1
|
|
|
|
|
F 67, B 265
|
0.163 |
|
Grade 2 |
Alpha grade for applications requiring max. ductility and formability. (more...) |
0.1
|
|
|
|
|
F 67, B 265
|
0.163 |
|
Grade 3 |
Alpha Phase C.P.Ti. Moderate strength with good formability. (more...) |
0.1
|
|
|
|
|
F 67, B 265
|
0.163 |
|
Grade 4 |
Alpha phase C, pure Ti. Highest strength of the CP grades. Used (more...) |
0.1
|
|
|
|
|
F 67, B 265
|
0.164 |
Alloy